Marginal fit of 3-unit implant-supported fixed partial dentures: Influence of pattern fabrication method and repeated porcelain firings.

BACKGROUND: Marginal fit significantly impacts the long-term success of dental restorations. Different pattern fabrication methods, including hand-waxing, milling, or 3D printing, may affect restorations accuracy. The effect of porcelain firing cycles on the marginal fit of metal-ceramic restorations remains controversial, with conflicting findings across studies. PURPOSE: The aim was to evaluate the potential effects of multiple porcelain firings (3, 5, 7 cycles) as well as pattern fabrication method (conventional hand-waxing, milling, and 3D printing) on the marginal adaptation of 3-unit implant-supported metal-ceramic fixed partial dentures. It was hypothesized that neither the wax pattern fabrication method nor repeated ceramic firings would significantly affect the marginal adaptation of metal-ceramic crowns. METHODS: In this in-vitro study, 30 Cobalt-Chromium alloy frameworks were fabricated based on pattern made through three techniques: conventional hand-waxing, CAD-CAM milling, and CAD-CAM 3D printing (n = 10 per group). Sixteen locations were marked on each abutment to measure the vertical marginal gap at four stages: before porcelain veneering and after 3, 5, and 7 firing cycles. The vertical marginal gap was measured using direct microscopic technique at ×80 magnification. Mean vertical marginal gap values were calculated and two-way ANOVA and Tukey's post hoc tests were used for inter-group comparisons (α = 0.05). RESULTS: The 3D printing group showed significantly lower (P<0.001) mean vertical marginal gaps (60-76 µm) compared to the milling (77-115 µm) and conventional hand-waxing (102-110 µm) groups. The milling group exhibited a significant vertical gap increase after 3 firing cycles (P<0.001); while the conventional (P = 0.429) and 3D printing groups (P = 0.501) showed no significant changes after 7 firing cycles. Notably, the vertical marginal gap in all groups remained below the clinically acceptable threshold of 120 µm. CONCLUSION: CAD-CAM 3D printing provided superior marginal fit compared to CAD-CAM milling and conventional hand-wax pattern fabrication methods. The impact of porcelain firing on the mean marginal gap was significant only in the milling group. All three fabrication techniques yielded clinically acceptable vertical marginal adaptation after repeated firings. Additive manufacturing holds promise to produce precise implant-supported prostheses.

The internal and marginal adaptation of lithium disilicate endocrowns fabricated using intra and extraoral scanners: An in-vitro study.

OBJECTIVES: The impression technique highly influences the adaptation of ceramic restorations. Not enough information is available to compare the marginal (MF) and internal fit (IF) of endocrowns fabricated with various digitization techniques. Therefore, this in-vitro study aimed to compare the MF and IF of lithium disilicate (LDS) endocrowns fabricated through direct and indirect digital scanning methods. MATERIALS AND METHODS: One extracted maxillary molar was used to fabricate endocrowns. The digitization of the model was performed with (G1) direct scanning (n = 10) utilizing an intraoral scanner (IOS), (G2) indirectly scanning the conventional impression taken from the model using the same IOS (n = 10), (G3) indirectly digitalizing the obtained impression using an extraoral scanner (EOS) (n = 10), and (G4) scanning the poured cast using the same EOS (n = 10). The MF and IF of the endocrowns were measured using the replica method and a digital stereomicroscope. The Kruskal-Wallis test was used to analyze data. RESULTS: The studied groups differed significantly (p<0.001). G2 (130.31±7.87 µm) and G3 (48.43±19.14 µm) showed the largest and smallest mean vertical marginal gap, respectively. G2 and G3 led to the highest and lowest internal gaps in all regions, respectively. With significant differences among the internal regions (p<0.001), the pulpal area demonstrated the most considerable misfit in all groups. CONCLUSIONS: Scanning the impression using an extraoral scanner showed smaller marginal and internal gaps.

A comparative evaluation of the variations on the shades of pressable ceramic system with the layering technique after different number of firing cycles: An in vitro study.

AIM: The main aim of the present study was to compare and evaluate the effect of repetitive firings on different shades of a pressable all ceramic system layered with veneering porcelain. SETTING AND DESIGN: In-vitro comparative study. MATERIALS AND METHODS: An in vitro comparative study was conducted, and a total of 60 disc shaped specimens (15 mm in diameter and 0.8 mm in thickness) were made of heat pressed ceramic of shades A2, A3, and B2 (20 discs of each shade) grouped as Group I, II, and III, respectively, using the lost wax technique. The discs were subsequently layered with veneering porcelain followed by glazing and overglazing and underwent a firing cycle at each step until six times combined. CIE L*a*b* measurements were noted on each sample after the third, fourth, fifth, and sixth firing using VITA Easyshade Advance 4.0 spectrophotometer. STATISTICAL ANALYSIS USED: Statistical Analysis was done by SPSS 17.0 software. One way analysis of variance, multiple comparisons using the Tukey test, and descriptive statistical analysis were done for all the groups in the study. P <0.05 was statistically significant. RESULTS: The mean color differences for the repeated firings were imperceptible (ΔE <1.67) to the human eye for all ceramic samples tested except between the fourth and fifth firing of Group II (shade A3). CONCLUSION: The analysis revealed that although repeated firings lead to changes in L*, a*, and b* values, the mean color difference was below the clinically acceptable color change (ΔE <3.7).

Fabrication trueness and internal fit of different lithium disilicate ceramics according to post-milling firing and material type.

OBJECTIVES: To evaluate whether post-milling firing and material type affect the fabrication trueness and internal fit of lithium disilicate crowns. METHODS: A prefabricated cobalt chromium abutment was digitized to design a mandibular right first molar crown. This design file was used to fabricate crowns from different lithium disilicate ceramics (nano-lithium disilicate (AM), fully crystallized lithium disilicate (IN), advanced lithium disilicate (TS), and lithium disilicate (EX)) (n = 10). Crowns, the abutment, and the crowns when seated on the abutment were digitized by using an intraoral scanner. Fabrication trueness was assessed by using the root mean square method, while the internal fit was evaluated according to the triple scan method. These processes were repeated after the post-milling firing of AM, TS, and EX. Paired samples t-tests were used to analyze the effect of post-milling firing within AM, TS, and EX, while all materials were compared with 1-way analysis of variance and Tukey HSD tests (α = 0.05). RESULTS: Post-milling firing reduced the surface deviations and internal gap of AM and EX (P ≤ 0.014). AM mostly had higher deviations and internal gaps than other materials (P ≤ 0.030). CONCLUSIONS: Post-milling firing increased the trueness and internal fit of tested nano-lithium disilicate and lithium disilicate ceramics. Nano-lithium disilicate mostly had lower trueness and higher internal gap; however, the maximum meaningful differences among tested materials were small. Therefore, the adjustment duration and clinical fit of tested crowns may be similar. CLINICAL SIGNIFICANCE: Tested lithium disilicate ceramics may be suitable alternatives to one another in terms of fabrication trueness and internal fit, considering the small differences in measured deviations and internal gaps.

The impact of chemical and hormonal treatments to improve seed germination and seedling growth of Juniperus procera Hochst. ex Endi.

Purpose: Juniper (Juniperus procera) is a common forest tree species in Saudi Arabia. The decline in many populations of J. procera in Saudi Arabia is mainly due to seed dormancy and loss of natural regeneration. This study assessed the effects of chemical and hormonal treatments on seed germination and seedling growth in juniper plants. Methods: The seeds were subjected to either chemical scarification with 90% sulfuric acid and 20% acetic acid for 6 min or hormonal treatment by seed soaking in two concentrations (50 and 100 ppm) of three growth regulators, namely, indole acetic acid (IAA), gibberellins (GA3), and kinetin, for 72 h. A control group without any seed treatment was also prepared. The experiments were performed in an incubator maintained at room temperature and under a light and dark period of 12 h for 6 w. The germinated seeds for each treatment were counted and removed from the dishes. The selected germinated seeds from different treatments were planted in a greenhouse and irrigated with tap water for another 6 weeks. The hormone-treated seedlings were sprayed with their corresponding hormone concentrations 1 w after planting. Results: The highest percentage of seed germination was significantly recorded after seed soaking in 50 ppm GA3, whereas treatment with IAA (100 ppm) resulted in the best seedling growth. Seedlings treated with the three phytohormones showed a significant increase in photosynthetic pigments, total soluble sugars, proteins, percentage of oil, IAA, GA3, and kinetin contents of juniper seedlings compared with the control value, whereas abscisic acid content was decreased compared with chemical treatments. Conclusion: The investigated different treatments had an effective role in breaking seed dormancy and improving seedling growth of J. procera, which is facing a notable decline in its population worldwide. Moreover, such an effect was more pronounced in the three phytohormones that succeeded in breaking dormancy and growth of the Juniperus plant than in the other treatments.

Tetracycline staining of the dentition: a review of the literature and report of a clinical case.

The present article reviews the literature regarding tetracycline staining of the dentition and its esthetic management. A total of 49 articles were identified in the initial search, and 22 articles met the eligibility criteria of this narrative literature review. Tetracycline staining results from its use in children between the ages of 6 months and 6 years, when tooth crowns are formed; the effects are dependent on the dosage, duration of treatment, stage of tooth mineralization, and activity of the mineralization process. Tooth bleaching is always the first treatment option for low-grade cases of tetracycline staining. Restorative procedures are indicated for severe staining. The article also describes the treatment of severe staining affecting the maxillary anterior dentition of a 48-year-old man who reported the systemic administration of tetracycline during childhood. Direct composite resin laminate veneers were proposed to achieve immediate, highly esthetic restorations. A combination of different resinous materials in different shades was applied to meet the needs of the patient. The use of direct composite resin laminate veneers satisfied the functional and esthetic demands of the patient at a lower cost than ceramic materials.

Ophthalmologists' assessment of the handling characteristics of the novel Finesse Reflex Handle in comparison to those of a conventional handle.

Internal limiting membrane (ILM) peeling requires a delicate handling technique. It is also important that ophthalmologists can use the ILM forceps handle of their preference. This study objectively and subjectively evaluated the handling of the novel Finesse Reflex Handle (Reflex) in comparison with that of a conventional handle. The force required to close the forceps tips, evaluated using a digital force gauge, was significantly lesser for Reflex than for the conventional handle (3.14 ± 0.09 N vs. 3.84 ± 0.06 N, P < 0.001). Twenty-one ophthalmologists with various levels of experience answered a questionnaire after using both handles, and the total questionnaire score for Reflex was higher than that for the conventional handle (35.0 ± 3.7 vs. 30.0 ± 6.9, P = 0.01). Furthermore, the duration of experience as an ophthalmologist was negatively correlated with the vertical motion, assessed by video analysis, for the conventional handle (P = 0.02, r = - 0.50) but not for Reflex (P = 0.26). In conclusion, objective and subjective analyses revealed that compared with the conventional handle, the novel Reflex handle had more favourable handling characteristics. Most ophthalmologists preferred the handling of Reflex. Reflex may compensate for a lack of surgical experience.

Biosafety and chemical solubility studies of multiscale crystal-reinforced lithium disilicate glass-ceramics.

Lithium disilicate (Li2 Si2 O5 ) glass-ceramics are currently a more widely used all-ceramic restorative material due to their good mechanical properties and excellent aesthetic properties. However, they have a series of problems such as high brittleness and low fracture toughness, which has become the main bottleneck restricting its development. Therefore, in order to compensate for these shortcomings, we propose to prepare a reinforced glass-ceramics with better mechanical properties and to test the biosafety and chemical solubility of the material. Li2 Si2 O5 whiskers were synthesized by a one-step hydrothermal method, and multi-scale crystal-enhanced Li2 Si2 O5 glass-ceramics were prepared by reaction sintering. The biosafety of multi-scale crystal-reinforced Li2 Si2 O5 glass-ceramics was investigated by in vitro cytotoxicity test, rabbit pyrogen test, mice bone marrow micronucleus test, skin sensitization test, sub-chronic systemic toxicity test, and chronic systemic toxicity test. Additionally, the chemical solubility of multi-scale crystal-reinforced Li2 Si2 O5 glass-ceramics was investigated. The test results showed that the material was non-cytotoxic, non-thermogenic, non-mutagenic, non-sensitizing, and non-systemic. The chemical solubility, determined to be 377 ± 245 µg/cm2 , complied with the ISO 6872 standard for the maximum solubility of ceramic materials. Multi-scale crystal-reinforced Li2 Si2 O5 glass-ceramics' biosafety and chemical solubility met current normative criteria, and they can move on to mechanical property measurements (such as flexural strength test, fatigue life test, friction and wear property study, etc.) and bonding property optimization, which shows promise for future clinical applications.

Componeer as an aesthetic treatment option for anterior teeth: a case report.

INTRODUCTION: Structural abnormalities or anomalies in the anterior teeth, also known as the aesthetic zone, are an important problem for patients and a challenge for dentists. Structural abnormalities or tooth anomalies can change in color, shape, and function. Most dentists prefer minimally invasive aesthetic treatment. One of the aesthetic treatment options for anterior teeth is veneers. Veneer is a restoration that covers the labial part of the tooth with a thin layer of material to correct abnormalities in the color, shape, or function of the tooth. Veneer restoration can be done indirectly with porcelain material made in a laboratory and directly with composite material on the tooth surface or prefabricated which is available from the factory. Componeer is a prefabricated composite veneer that combines the aesthetic properties of ceramic veneers and the adhesive ability of composite veneers to the tooth structure. This case report describes the treatment of two central incisors that had been filled with composite and peg shapes on both lateral incisors using a componeer. CASE REPORT: A 32-year-old female patient came to the Dental Conservation Clinic at Dentistry Hospital, Padjadjaran University with the main complaint of her right and left upper front teeth and wanted to repair her old fillings and close the gap between her right and left upper front teeth and her canine teeth. Clinical examination showed that teeth 11 and 21 had been filled with composite which had changed color and had an inharmonious shape as well as a gap between the upper front teeth on the right and left sides and the right and left canine teeth. TREATMENT: The maxilla and mandibular teeth are molded for study models and working models. In the working model, a wax-up is carried out, then a mock-up on the patient's teeth. Next, choose the color and size of the components that match the mock up results. Teeth 11 and 21 had their old composite fillings cleaned and refilled with dentin colored composite, teeth 13, 12, 11, 21, 22, and 23 were prepared with a minimum thickness of 0.3 mm to make room for the componeer material. The teeth was etched and bonded, and bonding was applied to the inner surface of the componeer. The composite is placed on the inner surface of the componeer then placed on the labial surface of the tooth and pressed with a special tool, then light cured. The final step is polishing. TREATMENT RESULTS: Teeth 13, 12, 11, 21, 22, and 23 which had undergone veneer treatment using componeer, were controlled after 1 week of treatment. The patient did not complain about the results of the treatment and said he was satisfied with the treatment.

Preparation of ultrathin translucent zirconia laminate veneers using 3D printing reduction guides.

Minimizing and controlling the amount of tooth reduction during the preparation of ultrathin laminate veneers is a challenge for minimally invasive dentistry. The use of reduction guides is advised to reach the optimal space required for the definitive restoration without excessive reduction. The digital production of a reduction guide used to control tooth preparation for ultrathin laminate veneers is described.

Surface treatments of the zirconia-reinforced lithium disilicate ceramic in the adhesion to the resin cement.

This study verified the effect of surface treatments of the zirconia-reinforced lithium disilicate ceramic bonded to resin cement. Ceramic blocks were divided according to treatments (n=10): FA+SRX (Fluoric acid + silane RX), FA+MDP (Fluoric acid + MDP), FA+SCF+MDP (Fluoric acid + silane CF + MDP), FA+MEP (Fluoric acid + MEP), and MEP (Self-etch primer). Resin cement cylinders were made in the ceramic blocks, photoactivated with 1,200 mW/cm² for 40s, stored in water at 37°C for 24h, and evaluated by the microshear strength test, optical failure descriptive analysis (%), surface characterization (SEM) and contact angle (Goniometer). Other samples were submitted to 10,000 thermocycles between 5°C and 55°C. Bond strength data were submitted to two-way ANOVA and Tukey's test. Contact angle to one-way ANOVA and Games-Howell's test (5%). At 24h, MEP showed higher bond strength, and FA+SRX the lower. FA+MDP and FA+SCF+MDP showed similar values and FA+MEP was intermediate. After thermocycling, FA+SCF+MDP, FA+MEP, and MEP showed higher values, and FA+SRX the lower while FA+MDP was intermediate. When the periods were compared, FA+MDP, FA+SCF+MDP, FA+MEP, and MEP showed higher values for 24h while FA+SRX was similar. SEM showed retentive surface and crystal exposure when treated with FA+SCF+MDP. The less retentive surface was obtained with MEP, and the other treatments promoted intermediate irregularities. In conclusion, surface treatment and thermocycling promoted different values of adhesive strength and contact angle in a zirconia-reinforced lithium silicate ceramic. Failures were predominantly adhesive, and the ceramic surface was characterized by different levels of roughness and selective exposure of crystals.

Effect of Ceramic Thickness on the Bond Strength to Resin-Luting Agents before and after Thermal Cycling.

This study investigated microshear bond strength (µSBS) of two (2) dual-cured resin-luting agents (RelyX™ Ultimate and RelyX™ U200) when photoactivated through varying thicknesses of lithium disilicate, with or without thermal cycling. Discs of IPS e.max Press of 0.5, 1.5, and 2 mm in thickness were obtained. Elastomer molds (3.0 mm in thickness) with four cylinder-shaped orifices 1.0 mm in diameter, were placed onto the ceramic surfaces and filled with resin-luting agents. A Mylar strip, glass plate, and load of 250 grams were placed over the filled mold. The load was removed and the resin-luting agents were photoactivated through the ceramics using a single-peak LED (Radii Plus.) All samples were stored in distilled water at 37oC for 24 h. Half of the samples were subjected to thermal cycling (3,000 cycles; 5ºC and 55ºC). All samples were then submitted to µSBS test using a universal testing machine (Instron 4411) at a crosshead speed of 0.5 mm/min. Data were submitted to three-way ANOVA and Tukey post-hoc test (α=0.05). The mean µSBS at 24 h was significantly higher than after thermal cycling (p<0.05). No statistical difference was found between resin-luting agents (p > 0.05). The mean µSBS for groups photoactivated through 0.5 mm ceramic were significantly higher than 1.5 mm and 2.0 mm (p < 0.05). In conclusion, increased ceramic thicknesses reduced the bond strength of tested resin-luting agents to lithium disilicate. No differences were found between resin-luting agents. Thermal cycling reduced the bond strength of both resin-luting agents.

Preheated acid associated with silane and electric current in the adhesion of the resin cement to ceramic.

This study verified the effect of the combination of preheated hydrofluoric acid/silane/electric current in the adhesion of the resin cement to ceramic. IPS E.max Press ceramic discs embedded in PVC rigid tubes were divided into four groups associating preheated hydrofluoric acid and silane applied with electrical current (n=10): Ha+S (Heated acid + silane); Ha+S+Ec (Heated acid + silane + electrical current); A+S (Acid + silane) and A+S+Ec (Acid + silano + electrical current). Resin cement/ceramic samples were stored in water at 37°C for 24h. After storage, they were submitted to the microshear test, fracture analysis, and contact angle at 24h or after thermocycling (10,000 cycles/5-55ºC). Bond strength data were evaluated by two-way ANOVA. For comparison between evaluation times (24h or thermocycling) was applied unpaired t-test. A significance post-hoc test of p=0.05 was assumed for analyses and graphs (GraphPad Prism 9.0 software). At 24h, the microshear strength showed similar values between Ha+S, Ha+S+Ec, and A+S+Ec groups, while A+S showed the lowest value with a statistical difference. After thermocycling, Ha+S and Ha+S+Ec were similar, as well as A+S and A+S+Ec. There was a significant difference in all groups comparing 24h (highest value) with after thermocycling (lowest value). Adhesive fracture was predominant in all groups and evaluation times. Ha+S and A+S groups showed higher contact angle values compared to the Ha+S+Ec and A+S+Ec with lower values. In conclusion, the association of preheated hydrofluoric acid/silane applied or not with electric current promoted different microshear strength values, fracture types, and contact angles in the resin cement/ceramic bond.

Effect of ceramic type and thickness on the masking ability of chairside machinable all-ceramic crowns.

OBJECTIVES: This study aimed to evaluate the influence of ceramic type and thickness on the masking ability and final aesthetic effects of chairside machinable all-ceramic crowns. METHODS: Six kinds from three types chairside machinable ceramic materials (IPS e.max CAD HT/MT/LT, IPS Empress LT, and VITA Suprinity HT/T) in shade A2 were fabricated to slice specimens into 1.0, 1.5, and 2.0 mm-thick sections (n=10). The color parameters of the specimens against black and white tiles and four resin substrates (A2, A4, B3, and C4 shade) were measured with a spectrophotometer. The translucency parameter (TP) was calculated using color parameters measured over standard white and black backgrounds. The color differences (ΔE) were calculated between there substrate shades (A4, B3, C4 ) and A2 shade (control group). Two-way analysis of variance (ANOVA) was performed on the TP values. The two va-riables were ceramic type and ceramic thickness. Three-way ANOVA was used to determine the effects of ceramic materials, ceramic thickness, and substrate shades on the ΔE values, followed by Tukey test for multiple comparisons (α=0.05). RESULTS: Ceramic type, ceramic thickness, and substrate shade significantly affected the ΔE values (P<0.001). The L* and b* values of the specimens increased with increasing ceramic thickness, except in substrate A2, whereas the ΔE values decreased. The color difference of all 1.0 mm-thick specimens or all specimens over the substrates C4 shade exceeded the clinically acceptable threshold (ΔE>3.3). CONCLUSIONS: The masking ability of chairside machinable all-ceramic crowns is influenced by ceramic type and thickness, and ceramic material. The thickness of ceramic less than 2.0 mm cannot mask the gray shade abutment.

Two-body wear of novel monolithic lithium-silicate ceramic materials and their corresponding different antagonists.

OBJECTIVES: Evaluation of the two-body wear of lithium-silicate ceramics against different antagonists compared to a direct resin composite and human teeth. METHODS: Initial LiSi Block [LISI], IPS e.max CAD [EMA], and CEREC Tessera [TESE] were investigated and compared with direct resin composite [FILL] and human teeth [tooth]. As antagonists were used: steatite, ceramic, and human enamel. The control group tooth was only tested with enamel antagonist. The combinations underwent thermomechanical aging using a chewing simulator. Material losses were calculated using GOM-analysis software. Kolmogorov-Smirnov test, Kruskal-Wallis H, Mann-Whitney-U-test with Bonferroni correction and Spearman-rho correlation were calculated. A fractographic analysis was performed. RESULTS: Within TESE, enamel antagonists led to lower restoration losses than steatite and ceramic antagonists. Within FILL, enamel and steatite antagonists caused lower material losses compared to ceramic antagonists. Against steatite antagonists, LISI showed lowest material losses. Against ceramic antagonists, the use of LISI led to lower material losses compared to FILL. Against tooth antagonists, TESE showed lower material losses than tooth and FILL and LISI lower than FILL. Within LISI, steatite antagonists showed lower material losses on the antagonist than ceramic. Within EMA, steatite antagonists showed higher material losses than ceramic ones. Within ceramic antagonists, LISI restoration material showed lower material losses than FILL and EMA. CONCLUSIONS: Regardless of the antagonist material, the material losses of LISI and EMA were comparable. However, the abrasion resistance of LISI tended to be higher than EMA. CLINICAL SIGNIFICANCE: LISI is a fully crystallized lithium-silicate ceramic and no longer needs to be processed after milling. In addition, the abrasion resistance is very good, regardless of the antagonist material chosen.

Accuracy of the intaglio surface of 3D-printed hybrid resin-ceramic crowns, veneers and table-tops: An in vitro study.

OBJECTIVES: The present study aims to examine the influence of the build angle on the accuracy (trueness and precision) of 3D printed crowns, table-tops and veneers with a hybrid resin-ceramic material. METHODS: One crown, on table-top and one veneer were printed in five different build angles (0°, 30°, 45°, 60°, 90°) (n = 50) with the digital light processing (DLP) system (Varseo XS, Bego) using hybrid resin (Varseo Smile Crownplus A3, Bego). All printed restorations were scanned using the laboratory scanner (D2000, 3Shape) and matched onto the initial reference design in metrology software (Geomagic Control X, 3D Systems). The root mean square error (RMSE) was calculated between the scanned and reference data. The data was statistically analyzed using the Tukey multiple comparison test and Wilcoxon multiple comparison test. RESULTS: The crown group showed higher trueness at 30° (0.021 ± 0.002) and 45° (0.020 ± 0.002), and table-tops at 0° (0.015 ± 0.001) and 30° (0.014 ± 0.001) (p < 0.0001). Veneers demonstrated higher trueness at 30° (0.016 ± 0.002) (p < 0.0001). All three restoration types demonstrated the lowest trueness at a 90° build angle and portrayed deviations along the z axis. The veneer and table-top groups showed the lowest precision at 90° (veneers: 0.021 ± 0.008; table-tops: 0.013 ± 0.003). The crown group portrayed the lowest precision at 45° (0.017 ± 0.005) (p < 0.0001). CONCLUSION: The build angle of DLP-printed hybrid resin-ceramic restorations influences their accuracy. CLINICAL SIGNIFICANCE: Considering the build angle is important to achieve a better accuracy of 3D-printed resin-ceramic hybrid restorations. This may help predict or avoid the interference points between a restoration and a die and minimize the clinical adjustments.

Influence of crown shade, translucency, and scan powder application on the trueness of intraoral scanners.

OBJECTIVES: Natural teeth and dental restorations present with various shades and levels of translucency. This study aimed to determine whether these variations in ceramic crowns and scan powder application affect the trueness of intraoral scanners. METHODS: Eight identical premade resin typodonts, each prepared for a crown on the maxillary right second molar, were used. Eight lithium disilicate crowns, distinguished by two levels of translucency (high and low) and four shades (BL1, A2, A3, and A4), were fabricated to an identical design and cemented onto each typodont, providing eight distinct experimental groups (2 levels of translucency × 4 shades). Reference scans were acquired using a desktop scanner. Test scans were performed ten times for each experimental group using two different intraoral scanners (Medit i700 and CEREC Primescan AC), with and without the application of scan powder (n = 10). Three-dimensional metrology software was used to assess the trueness of the intraoral scan datasets. Statistical analysis involved the Kruskal-Wallis H test, Mann-Whitney U test, and independent t-test (α=0.05). RESULTS: For powder-free intraoral scan datasets, the crown shade did not significantly affect trueness within each translucency group (P = 1.000). For both intraoral scanners, compared with low translucency groups, higher marked deviations were exhibited by high translucency groups (P<.001). Scan powder use largely mitigated these differences (P>.05) and enhanced the trueness of the intraoral scan (P<.01). CONCLUSIONS: Shade did not significantly influence the trueness of intraoral scans. High-translucency crowns were scanned with less accuracy than were low-translucency crowns. CLINICAL SIGNIFICANCE: Unlike tooth shade, translucency significantly affected the accuracy of intraoral scans. Therefore, considering the use of scan powder when scanning objects with high translucency may be beneficial.

Fracture resistance of CAD/CAM endocrowns made from different materials in maxillary premolar interproximal defects.

OBJECTIVES: This in vitro study aims to compare the fracture resistance of three CAD/CAM materials used in endocrown restoration of interproximal defects in maxillary premolars. MATERIALS AND METHODS: 45 maxillary premolars extracted as part of orthodontic treatment were included. Following standardized root canal treatment, all teeth were prepared into Mesial-Occlusal (MO) cavity types. The samples were then randomly divided into three groups: LD [repaired with lithium disilicate glass ceramics (IPS e.max CAD)], VE [treated with polymer-infiltrated ceramics (Vita Enamic)], and LU [repaired with resin-based nanoceramics (Lava Ultimate)]. Axial static loading was applied using a universal testing machine at 1 mm/min until fracture, and fracture resistance and failure modes were recorded. RESULTS: Regarding Fracture Resistance Values (FRVs), the LD group exhibited significantly higher values than the other two groups, VE (P = 0.028) and LU (P = 0.005), which showed no significant difference (P = 0.778). On the other hand, regarding failure modes, the LD group had a higher prevalence of irreparable fractures compared to the other two groups, VE (P < 0.001) and LU (P < 0.001), which showed no significant difference. CONCLUSIONS: Although lithium disilicate glass ceramics exhibited higher FRVs, they had a lower repair probability. In contrast, polymer-infiltrated ceramics and resin-based nanoceramics contributed to tooth structure preservation. CLINICAL RELEVANCE: For maxillary premolars with interproximal defects following root canal treatment, resin ceramic composites are recommended for restoration to enhance abutment teeth protection.